Isolation And Characterization Of Cassava Fibre For Tissue Engineering Scaffold Application

Thumbnail Image

Date

2017-07

Journal Title

Journal ISSN

Volume Title

Publisher

University of Ghana

Abstract

Cassava bagasse and its extracted cellulose fibres have seen frequent application mostly in the packaging industry as reinforcement material in plastic composites development. However, the material properties such as the mechanical properties of the single elementary cassava cellulose fibres have not been examined and reviewed literature does not show its potential use in the development of tissue engineering scaffolds for cell culture. The study, therefore, characterized the mechanical properties, physicochemical, morphological and microstructural characteristics and thermal degradation profiles of single elementary cellulose fibre as well as the central vascular fibre (“thick-core fibre) isolated from three genotypes of cassava (tagged in this study as ID4, ID6 and AF). Additionally, the study examined the effect of incorporating cassava cellulose microfibres as reinforcement on the mechanical properties and microstructure characteristics of three-dimensional gelatin scaffolds. Non-treated isolated cassava fibres were tested according to ASTM C1557. Three-dimensional cassava microfibre/gelatin scaffolds with different fibre weight fractions were fabricated using phase separation and freeze-drying methods. Tensile test results showed that there was no significant difference (p > 0.05) in mechanical properties recorded between the single elementary fibre and vascular fibre (thick-core) for the three cassava genotypes. Different genotypes of cassava fibre showed significant differences (p < 0.05) in tensile strength and Young’s modulus, with ID4 fibre recording the highest average tensile strength of 7.567 ± 3.844 MPa and highest elastic modulus of 336.485 ±130.803 MPa. XRD analysis showed similar diffraction pattern with minimal variation in signal intensities for both single and thick-core fibres for all cassava genotypes suggesting nonsignificant differences in crystalline structure between them. TGA analysis showed that cassava fibre is thermally stable between the temperatures of 100 °C – 200 °C. The cassava cellulose microfibre/gelatin scaffolds fabricated showed rough surfaces compared to pure gelatin scaffolds and were highly porous with surface porosity ranging between 84 and 90%, and had interconnected pores of average size 36 ±12 μm. Gelatin scaffolds containing up to 7% cassava cellulose microfibre load recorded a maximum compressive strength of 0.29±0.02 MPa, about eight (8) times higher than that for the pure gelatin scaffolds and average Young’s modulus of 1.31 ±0.03 MPa, about four times higher than pure gelatin scaffolds. Preliminary theoretical modelling using Halpin-Tsai model could accurately explain the variabilities in the compression modulus of the gelatin composite scaffolds. In all, the results showed that cassava fibre has considerable mechanical strength and stiffness and can be used as reinforcement filler to improve the mechanical integrity of tissue engineering polymer scaffolds. The cassava fibre/gelatin scaffolds showed surface architecture that could improve cell–matrix adhesion and efficient cell seeding and diffusion of nutrients during cell culture.

Description

Thesis (MPhil)

Keywords

Isolation, Characterization, Cassava Fibre, Tissue Engineering Scaffold Application

Citation

Endorsement

Review

Supplemented By

Referenced By